Duplex Zero-halogen flame-retardant POF Cable
Zero-halogen flame-retardant POF cable is the products Hwaying developed for industrial application. Similar with normal POF cable, Zero-halogen flame-retardant POF cable is made of plastic optical fiber, which is excellent short data transmission medium, with special anti-flaming sheath coated. Plastic optical cable is immune to electromagnetic wave radiation, noise, and has a good capacity of resisting distance. Plastic optical fibers have a higher bandwidth than other transmission material like copper, while it is energy-saving and environment protection.
Feature
1. Easy install and repair
2. Can operate under high/low temperature
3. Energy-Saving and enviromental friendly
4. Available in fully dielectric version
5. Immunity from electromagnetic interferences
6. Also available in fully dielectric version
|
|
|
HPFC104460-VT |
|||
|
Item |
Specification |
||||
|
Min. |
Typ. |
Max. |
|||
|
Optical Fiber |
Core Material |
Polymetyl-Methacrylate Resin |
|||
|
Clad Material |
Fluorinated Polymer |
||||
|
Core Reflective Index |
﹣ |
1.49 |
﹣ |
||
|
Clad Reflective Index |
﹣ |
1.41 |
﹣ |
||
|
Reflective Index Profile |
Step Index |
||||
|
Numerical Aperture (NA) |
﹣ |
0.5 |
﹣ |
||
|
Core Diameter [um] |
920 |
980 |
1040 |
||
|
Clad Diameter [um] |
940 |
1000 |
1060 |
||
|
First Jacket |
Material |
POLYETHYLENE |
|||
|
Diameter [mm] |
2.2±0.07 |
﹣ |
4.4±0.2 |
||
|
Color |
Black |
||||
|
Second Jacket |
Material |
POLYVINY CHLORIDE |
|||
|
Diameter [mm] |
5.7 |
6.00 |
6.3 |
||
|
Color |
Gray |
||||
|
Indication on the product |
﹣ |
||||
|
Indication of UL Style No. |
﹣ |
||||
|
Inflammability (VW-1 Test Method) |
VW-1 Test Method |
||||
|
Approximate Weight [g/m] |
32 |
||||
1. Performance
|
|
|
HPFC104460-VT |
||||
|
Item |
Specification |
|||||
|
Min. |
Typ. |
Max. |
||||
|
Maximum Rating |
Storage Temperature[℃] |
No Physical Change |
-50 |
﹣ |
80 |
|
|
Operation Temperature[℃] |
No Deterioration in Optical Properties |
-50 |
﹣ |
80 |
||
|
Operation Temperature Under 95% RH [℃] |
No Deterioration in Optical Properties |
﹣ |
﹣ |
80 |
||
|
Transmission loss |
Attenuation (collimated light) [dB/km] |
650nm |
﹣ |
﹣ |
180 |
|
|
(Ta=25℃) |
||||||
|
650nm |
﹣ |
﹣ |
200 |
|||
|
(Ta:Operation Temp.) |
||||||
|
Mechanical Properties |
Minimum Bending Radius [mm] |
No Physical and Optical Change |
25 |
﹣ |
﹣ |
|
|
Repeated Bending Times |
(±＜90° R=15mm) |
10000 |
﹣ |
﹣ |
||
|
Tensile Strength |
Tensile Test Equipment |
14 |
﹣ |
﹣ |
||
|
[kg] |
||||||
|
Maximum Twisting Times |
L=1m Restoration |
5 |
﹣ |
﹣ |
||
|
Drop Impact Strength [cm] |
2kg OD20mm cylinder drop |
5 |
﹣ |
﹣ |
||
All tests are carried out under temperature of 25℃ unless otherwise specified.
* Attenuation change shall be within 10% after 1,000 hours.
** Attenuation change shall be within 10% after 1,000 hours, except that due to absorbed water.